Aquolin 270 is a water dispersible polyisocyanate based on hexamethylene diisocyanate (HDI). In combination with waterborne polyurethane, polyacrylate, etc., it can be used for water-borne coatings and adhesives. After addition of Aquolin 270, the ready-to-use mixture must be used within the pot life.
Aquolin 270 can be diluted with the solvents, such as propylene glycol methyl ether acetate (PMA), propylene glycol diacetate (PGDA), butyl acetate, etc. Only PU grade solvents (< 0.05% water) should be used and the solvents must be tested in advance by the user to determine suitability.
Properties：
High gloss and high building up.
Excellent weather resistance.
Excellent water dispersible and hand-mixing.
Characteristic data*
Property
Value
Unit
Method
Appearance
Colorless to yellowish transparent liquid
NCO content
21.5±0.5
%
GB/T 12009.4-2016
Viscosity
1500-3500
mPa·s
Brookfield LV, 63#/3rpm,25°C
Color APHA
＜80
GB/T 1722-1992
Monomeric
isocyanate
≤ 0.2
%
GB/T 18446-2009
Flash point
~196
°C
GB/T 5208
Density
~1.16
g/cm3
GB/T 4472-2011
*These properties are typical but do not constitute specifications.
Storage：
The product should be stored in dry conditions above 5°C and below 35°C with the integrity of the packaging, and prevent direct sunlight. The validity of this product is for 12 months, performance assessment is recommended before use after shelf life. The product should be protected from freezing during storage. Water dispersible polyisocyanates are very moisture-sensitive and react with water to form carbon dioxide and insoluble ureas. The generation of carbon dioxide can lead to dangerous increases in pressure. The containers must always be kept tightly closed and the access of water in all forms must be prevented. It is suggested to use up oncethe package is open.
Packaging:
200KG/drum Please fasten the packaging cover as soon as possible after original packaging to prevent the mixing of other substances such as moisture and other substances that may affect the performance of the product. Do not inhale dust, avoid skin and mucous membrane contact. Smoking, eating and drinking are prohibited in the workplace. After work, shower and change clothes. Store contaminated clothes separately and reuse them after washing. Maintain good hygiene practices.
Aquolin 269 is a water dispersible polyisocyanate based on hexamethylene diisocyanate (HDI). In combination with waterborne polyurethane, polyacrylate, etc., it can be used for water-borne coatings and adhesives. After addition of Aquolin 269, the ready-to-use mixture must be used within the pot life.
Properties：
High gloss and high building up.
Excellent water resistance.
Excellent water dispersible and hand-mixing.
Excellent weather resistance.
Characteristic data*
Property
Value
Unit
Method
Appearance
Colorless to yellowish transparent liquid
NCO content
18.8-19.8
%
GB/T 12009.4-2016
Viscosity
500-2000
mPa·s
Brookfield LV, 63#/3rpm,25°C
Color APHA
＜80
GB/T 1722-1992
Monomeric
isocyanate
≤ 0.2
%
GB/T 18446-2009
Flash point
~128
°C
GB/T 5208
Density
~1.13
g/cm3
GB/T 4472-2011
*PThese properties are typical but do not constitute specifications.
Storage：
The product should be stored in dry conditions above 5°C and below 35°C with the integrity of the packaging, and prevent direct sunlight. The validity of this product is for 12 months, performance assessment is recommended before use after shelf life. The product should be protected from freezing during storage. Water dispersible polyisocyanates are very moisture-sensitive and react with water to form carbon dioxide and insoluble ureas. The generation of carbon dioxide can lead to dangerous increases in pressure. The containers must always be kept tightly closed and the access of water in all forms must be prevented. It is suggested to use up once the package is open.
Packaging:
200KG/drum Please fasten the packaging cover as soon as possible after original packaging to prevent the mixing of other substances such as moisture and other substances that may affect the performance of the product. Do not inhale dust, avoid skin and mucous membrane contact. Smoking, eating and drinking are prohibited in the workplace. After work, shower and change clothes. Store contaminated clothes separately and reuse them after washing. Maintain good hygiene practices.
Aquolin 268 is a water dispersible polyisocyanate based on hexamethylene diisocyanate (HDI). In combination with waterborne polyurethane, polyacrylate, etc., it can be used for water-borne coatings and adhesive. After addition of Aquolin 268, the ready-to-use mixture must be used within the pot life.
Aquolin 268 can be diluted with the solvents, such as propylene glycol methyl ether acetate (PMA), propylene glycol diacetate (PGDA), butyl acetate, etc. Only PU grade solvents (< 0.05% water) should be used and the solvents must be tested in advance by the user to determine suitability.
Properties：
High gloss and high building up.
Excellent weather resistance.
Characteristic data*
Property
Value
Unit
Method
Appearance
Colorless to yellowish transparent liquid
NCO content
%
GB/T 12009.4-2016
Viscosity
20.5±0.5
mPa·s
Brookfield LV, 63#/3rpm,25°C
Color APHA
5000-7000
GB/T 1722-1992
Monomeric
isocyanate
≤0.1
%
GB/T 18446-2009
Flash point
~196
°C
GB/T 5208
Density
~1.17
g/cm3
GB/T 4472-2011
*These properties are typical but do not constitute specifications.
Storage：
The product should be stored in dry conditions above 5°C and below 35°C with the
integrity of the packaging, and prevent direct sunlight. The validity of this product is for
12 months, performance assessment is recommended before use after shelf life. The product should be protected from freezing during storage. Water dispersible polyisocyanates are very moisture-sensitive and react with water to form carbon dioxide and insoluble ureas. The generation of carbon dioxide can lead to dangerous increases in pressure. The containers must always be kept tightly closed and the access of water in all forms must be prevented. It is suggested to use up once the package is open.
Aquolin 161 is a water dispersible polyisocyanate based on hexamethylene diisocyanate (HDI). In combination with water-borne polyurethane, polyacrylate, etc., it can be used for adhesive products toimprove the resistance to hydrolysis and heat. It also can be used for waterborne coatings. After addition of Aquolin 161, the ready-to-use mixture must be used within the pot life.
Aquolin 161 can be diluted with the solvents, such as propylene glycol methyl ether acetate (PMA), propylene glycol diacetate (PGDA), butyl acetate, etc. Only PU grade solvents (< 0.05% water) should be used and the solvents must be tested in advance by the user to determine suitability.
Product Features:
Excellent resistance
Long pot life
Good gloss and building up
Characteristic Data* :
Property
Value
Unit
Method
Appearance
Transparent to
light yellow liquid
NCO content
18.2-19.2
%
GB 12009.4-2016
Viscosity (25°C)
1500-3500
mPa·s
GB/T 2794-2013
(Brookfield LV,63#/12rpm)
Color APHA
<60
GB/T 1722-1992
Monomeric
isocyanate
≤0.1
%
GB/T 18446-2009
Flash point
~226
%
GB/T 5208-2008
Density
~1.16
g/cm3
GB/T 4472-2011
*Property values represent typical results only and are not to be considered as specifications,subject to specific COA
Storage:
The product should be stored in dry conditions above 5°C and below 35°C with the integrity of the packaging, and prevent direct sunlight. The validity of this product is for 12 months, performance assessment is recommended before use after shelf life. The product should be protected from freezing during storage. Water dispersible polyisocyanates are very moisture-sensitive and react with water to form carbon dioxide and insoluble ureas. The generation of carbon dioxide can lead to dangerous increase s in pressure. The containers must always be kept tightly closed and the access of water in all forms must be prevented. It is suggested to use up once the package is open.
Packaging:
200KG/drum Please fasten the packaging cover as soon as possible after original packaging to prevent the mixing of other substances such as moisture and other substances that may affect the performance of the product. Do not inhale dust, avoid skin and mucous membrane contact. Smoking, eating and drinking are prohibited in the workplace. After work, shower and change clothes. Store contaminated clothes separately and reuse them after washing. Maintain good hygiene practices.
Curing speed of MF-K60X is faster than that of melamine.
Storage stability of paint using MF-K60X
1. Formulation : Polyol : Acrylic Polyol A801
(manufactured and sold by DIC OHV = 100 mgKOH/g Resin )
·Blocked Polyisocyanate : DURANATETM MF-K60X
·NCO OH = 1.0
2. Storage condition : 40’C under Nitrogen
3.Measurement of Viscosity : Ford Cup #4 at 20°C
Storage and Transportation:
STORAGE: It is recommended to store in a dry and cool area with proper ventilation.
Packaging:
200KG/drum Please fasten the packaging cover as soon as possible after original packaging to prevent the mixing of other substances such as moisture and other substances that may affect the performance of the product. Do not inhale dust, avoid skin and mucous membrane contact. Smoking, eating and drinking are prohibited in the workplace. After work, shower and change clothes. Store contaminated clothes separately and reuse them after washing. Maintain good hygiene practices.
Blocked aliphatic HDI-polyisocyanate. To formulate lightfast one-component stoving polyurethane coatings with high themal yellowing resistance; as an additive to improve flexibility and adhesion.
Desmodur BL 3370 MPA is a blocked aliphatic polyisocyanate based on hexamethylene diisocyanate (HDI).
It is suitable for use in combination with Desmophen® grades to formulate lightfast, one-component stoving polyurethane coatings with high resistance to thermal yellowing; as an additive in conventional stoving coating systems to improve the reactivity, flexibility and adhesion.
Storage Conditions:
Desmodur BL 3370 MPA should be stored in tightly sealed original containers and protected from moisture, heat, and foreign materials. Storage at higher temperatures will result in increase of color and viscosity. Storage at significant lower temperatures will result in solidification. This solidification is reversible by briefly heating the product without adversely affecting the quality of the product. Recommended storage temperature is 0º-30ºC.
Characteristics:
Property Name
Test Method
Unit
Value
Density
g/cm^3
approx. 1.08
Viscosity at 25^oC
mPa∙s
approx. 3,200
Equivalent weight
approx. 470
Flash point
°C
approx. 49
Blocked NCO content
%
approx. 8.9
Specifications:
Property Name
Test Method
Unit
Value
Non-volatile content (1 g / 60 min / 80^oC)
%
70 ± 3
Free NCO content
%
≤ 0.2
Viscosity at 23°C
mPa∙s
3,800 ± 1,200
Hazen color value
≤ 60
Packaging:
200KG/drum Please fasten the packaging cover as soon as possible after original packaging to prevent the mixing of other substances such as moisture and other substances that may affect the performance of the product. Do not inhale dust, avoid skin and mucous membrane contact. Smoking, eating and drinking are prohibited in the workplace. After work, shower and change clothes. Store contaminated clothes separately and reuse them after washing. Maintain good hygiene practices.
Blocked aliphatic polyisocyanate based on HDI.In combination with polyol components for the formulation of lightfast one-component polyurethane stoving coatings.
Desmodur PL 350 MPA/SN is a blocked aliphatic polyisocyanate based on HDI.
It is suitable for use in combination with polyol components for the formulation of lightfast one-component polyurethane stoving coatings.
Storage Conditions:
Desmodur PL 350 MPA/SN should be stored in tightly sealed original containers and protected from moisture, heat, and foreign materials. Storage at higher temperatures will result in increase of color and viscosity. Storage at significant lower temperatures will result in solidification. This solidification is reversible by briefly heating the product without adversely affecting the quality of the product. Recommended storage temperature is 0º-30ºC.
Characteristics:
Property Name
Test Method
Unit
Value
Blocked NCO content
%
approx. 10.5
Density at 20°C
g/cm^3
approx. 1.10
Flash point
°C
approx. 53
Equivalent weight
approx. 400
Specifications:
Property Name
Test Method
Unit
Value
Non-volatile content (0.2 g / 60 min / 80^oC)
%
75 ± 2
Color value
≤ 100
Viscosity at 23^oC
mPa∙s
4,300 ± 1,500
Packaging:
200KG/drum Please fasten the packaging cover as soon as possible after original packaging to prevent the mixing of other substances such as moisture and other substances that may affect the performance of the product. Do not inhale dust, avoid skin and mucous membrane contact. Smoking, eating and drinking are prohibited in the workplace. After work, shower and change clothes. Store contaminated clothes separately and reuse them after washing. Maintain good hygiene practices.
Blocked aliphatic polyisocyanate based on HDI.In combination with Desmophen® grades to formulate lightfast, one-component stoving polyurethane coatings.
In combination with Desmophen® grades to formulate lightfast, one-component stoving polyurethane coatings.
Storage Conditions:
– Storage in original sealed Covestro container.
– Recommended storage temperature: 0 – 30 °C.
– Protect from moisture, heat and foreign material.
General information: Storage at higher temperatures will result in increase of color and viscosity. Storage at significant lower temperatures will result in solidification. This solidification is reversible by briefly heating the product without adversely affecting the quality of the product.
Sampling:
No data available
Characteristics:
Property Name
Test Method
Unit
Value
Flash point
DIN EN ISO 13 736
°C
approx. 53
NCO content, blocked
%
approx. 10.5
Equivalent weight
approx. 400
Density at 20 °C
DIN EN ISO 2811
g/ml
approx. 1.1
Specifications:
Property Name
Test Method
Unit
Value
Non-volatile content (0.2 g/60 min/80 °C)
DIN EN ISO 3251
%
75 ± 2
Viscosity at 23 °C
DIN EN ISO 3219/A.3
mPa*s
3,600 ± 1,000
Hazen color value
DIN EN 1557
≤ 100
Packaging:
200KG/drum Please fasten the packaging cover as soon as possible after original packaging to prevent the mixing of other substances such as moisture and other substances that may affect the performance of the product. Do not inhale dust, avoid skin and mucous membrane contact. Smoking, eating and drinking are prohibited in the workplace. After work, shower and change clothes. Store contaminated clothes separately and reuse them after washing. Maintain good hygiene practices.
# Automobile, motorcycle; base coat and top coat# Heavy duty coatings
Typical properties：
Appearance
Colorless to slightly yellowish clear liquid
Non-volatile
75 wt%
Solvent
Methoxypropylacetate (PMA)Xylene=1/1
NCO content
16.5 wt%
Viscosity
210mPa .s at 25°C
Color value
<1 (Gardner)
NCO equivalent weight
Approx.254
Flash point
39°C
Density at 20°C
1.07
These values provide general information and are not part of the product specifications.
Stability / thinnability:
DURANATETM 22A-75PX can be thinned with esters, ketones and aromatic.hydrocarbons such as ethyl acetate, butyl acetate, methoxypropylacetate (PMA),methyl ethyl ketone, methyl-butyl ketone, cyclohexanone, toluene, xylene, Solvesso#100 and mixture thereof. Generally speaking, it has good compatibility with thesolvents mentioned. However, the solutions formed must be tested for their storagestability.
Only PU grade solvents can be used (max. 0.05% water, absence of reactive groupssuch as hydroxyl or amines groups). Aliphatic hydrocarbons such as hexane,cyclohexane, methylcyclohexanes and mineral spirits, are unsuitable as solventsbecause of their poor solubility.
DURANATETM 22A-75PX should not be thinned to below a solid content of 40%.Prolonged storage of solution with lower solid content may result in turbidity andsedimentation.
Compatibility:
Mixing ratio of DURANATETM 22A-75PX with polyols is based on NCO/OH equivalentratio of 1/1 .
Storage:
DURANATETM 22A-75PX is sensitive to moisture and should therefore always bestored in sealed containers.
CORONATE® HX-T by Tosoh is polyisocyanate. It is a non-yellowing compound containing HDI rings, modified by multifunctional alcohols. Used as a binding agent for substrates. Suitable for PU coatings. Designed for automotive, construction, wooden, metal, plastic, rubber, concrete, paper and leather coatings. It can be used in combination with NIPPOLANS or polyols (polyesters, epoxies, acrylics and other resins.
Storage and Transportation:
STORAGE: It is recommended to store in a dry and cool area with proper ventilation.
Packaging:
200KG/drum Please fasten the packaging cover as soon as possible after original packaging to prevent the mixing of other substances such as moisture and other substances that may affect the performance of the product. Do not inhale dust, avoid skin and mucous membrane contact. Smoking, eating and drinking are prohibited in the workplace. After work, shower and change clothes. Store contaminated clothes separately and reuse them after washing. Maintain good hygiene practices.