INV high primary hydroxylated modified polyether polyol P1000 P2000

Published by BDMAEE on 2023-12-12

P-1000 P-2000 is a high primary hydroxylated modified polyether polyol. Compared with ordinary polyether polyols, it has the characteristics of high reactivity, high mechanical strength and good water resistance and weather resistance. Widely used in polyurethane resin synthesis, adhesives, elastomers, coatings, etc.

Basic parameters

Project	Unit	Specifications
Project	Unit	P-1000	P-2000
Appearance Moisture pH hydroxy value Viscosity acid value	VISUAL % Triol mgKOH/ g 25℃ , mPa.s mgKOH/ g	Transparent liquid 0.05 MAX After 3 days of weathering test	Tear strength (MPa)	24	16	55
Strength retention%		81	75	93

Sample conditions
Device:SUPER UV TESTER; Light source: Metal halide mercury lamp; Irradiation intensity: 75mW/cm²; Irradiation temperature: 73°C 50%Rh×3.8hr; 38°C 95%Rh×1hr for 3 days (15 cycles).

Strength retention rate after water resistance test:

Project		P-2000	PP-2000	PTMEG2000
Early days	Tear strength (MPa)	30	21	59
After 5 days of weathering test	Tear strength (MPa)	20	9	56
Strength retention%		68	44	95

Experimental conditions: Soak in NaOH 10%wt solution for 5 days at 70°C.

ht:0.0000pt; text-align:center”>59

After 5 days of weathering test

Tear strength (MPa)

Strength retention%

Experimental conditions: Soak in NaOH 10%wt solution for 5 days at 70°C.

Categories: Application Tags: INV high primary hydroxylated modified polyether polyol P1000 P2000