Cashew nut shell liquid bio-based modified polyol FX-9007

Cashew nut shell liquid bio-based modified polyol FX -9007

Guangzhou Polycarbon provides a series of renewable polyol products for polyurethane formulations.

Cashew nut shell liquid products demonstrate excellent water resistance, low moisture sensitivity, and balanced mechanical strength.

Cashew nut shell liquid polyols provide excellent chemical resistance, especially alkali resistance.

Main markets include coatings, adhesives, potting, foam and composite materials.

Mechanical properties

Recipe

FX -9007/PMDI

= 100/40.3

Tensile strength(MPa)

17.3

ShaoDHardness

71

Lap shear strength, (MPa)

10.7

Elongation at break(%)

84

Tg(°C)

23.2

Cure conditions

Room temperature 7

Curing speed

Recipe

FX -9007/PMDI

= 100/40.3

Hard work(hours)at 25°C

4.5

Hard work(hours)at 5°C

17.3

Hard work(hours)at 0°C

22.7

Hydrolytic stability

Polyol samples, and polymerizationMDICure

NCOIndex=100)

FX-9007

Lap shear strength (MPa), Control sample

8.7

80°C/7 After Tianshui immersion test

Lap shear strength (MPa)

6.2

Lap shear strength decreases(%)

28.5

Lap shear strength (MPa), Control sample

8.7

80°C/7 After Tianshui immersion test

Lap shear strength (MPa)

6.2

Lap shear strength decreases(%)

28.5

BDMAEE:Bis (2-Dimethylaminoethyl) Ether

CAS NO:3033-62-3

China supplier

For more information, please contact the following email:

Email:sales@newtopchem.com

Email:service@newtopchem.com

Email:technical@newtopchem.com

BDMAEE Manufacture !